ABS-Like · grade
ABS-Like-ESD
Properties of the ESD condition, compared with the other ABS-Like grades.
For electronics trays, nests and handling fixtures that must not build up static charge.
What is ABS-Like-ESD?
ABS-Like-ESD is ABS-Like in the ESD grade — for electronics trays, nests and handling fixtures that must not build up static charge. ABS-Like-ESD has a yield strength of 45 MPa (6.53 ksi) and a tensile strength of 48 MPa (6.96 ksi) — weaker than 65% of polyurethane grades. Elongation at break is 8% and the elastic modulus is 2.2 GPa (0.319 Msi). ABS-Like-ESD has a density of 1.18 g/cm³ (0.0426 lb/in³), heavier than 87% of polyurethane grades. Its glass-transition temperature is 62°C (144 °F). STD is the default condition FabDigit quotes; ESD is available on request or by drawing note.
Limitations
- High embodied carbon — 6.5 kg CO₂/kg, worse than 100% of polyurethane grades
- Limited service temperature — 55°C (131 °F), worse than 96% of polyurethane grades
- Low fracture toughness — 1.3 MPa·√m (1.18 ksi·√in), worse than 90% of polyurethane grades
- High mold shrinkage — 0.6%, worse than 75% of polyurethane grades
ABS-Like-ESD properties
Typical room-temperature values for ABS-Like-ESD — 8 properties are specific to this condition; the rest are grade-level values shared by every ABS-Like grade. Each bar shows where the value sits among the polyurethane grades in FabDigit's library — further right is higher.
Physical5
ABS-Like-ESD has a density of 1.18 g/cm³ (0.0426 lb/in³), heavier than 87% of polyurethane grades. Its glass-transition temperature is 62°C (144 °F).
Mechanical16
ABS-Like-ESD has a yield strength of 45 MPa (6.53 ksi) and a tensile strength of 48 MPa (6.96 ksi) — weaker than 65% of polyurethane grades. Elongation at break is 8% and the elastic modulus is 2.2 GPa (0.319 Msi).
Thermal10
ABS-Like-ESD is rated for continuous service to 55°C (131 °F). It conducts heat at 0.2 W/m·K (0.116 BTU/hr·ft·°F), worse than 57% of polyurethane grades. Thermal expansion is 90 µm/m·K (50 µin/in·°F).
Electrical6
ABS-Like-ESD is an electrical insulator with a dielectric strength of 18 kV/mm (457.2 V/mil) and a resistivity of 1×10⁷ Ω·m.
Chemical & Environmental3
Corrosion resistance is good (68/100), worse than 87% of polyurethane grades. UV resistance is poor.
Sustainability4
Producing a kilogram of ABS-Like-ESD takes about 120 MJ of energy and emits 6.5 kg of CO₂ — more than 98% of polyurethane grades. Typical recycled content is 0%.
Manufacturability6
ABS-Like-ESD's machinability is good (55/100, worse than 67% of polyurethane grades); weldability not recommended (5/100); formability not recommended (5/100).
Values are nominal handbook figures for design screening. Certified mill or lot data ships with every FabDigit order on request.
Other ABS-Like grades and fills
ABS-Like is also supplied in 6 other conditions. The full side-by-side table is on the ABS-Like overview.
- STDDefaultDefault choice for appearance models, fit-check parts and general functional prototypes at room temperature.52 MPa tensile
- HTUse for parts seeing hot air, near-motor housings, paint-bake or short thermal excursions above 80 °C.62 MPa tensile
- RIGIDChoose for stiff, dimensionally stable jigs, fixtures and thin ribs where deflection matters more than toughness.62 MPa tensile
- BIOUse where ISO 10993 skin/mucosa contact certification is required — surgical guides, dental models, wearable fit parts.55 MPa tensile
- FRRequired for electrical enclosures, rail/aero interior mock-ups and any part needing a UL 94 V-0 rating.48 MPa tensile
- ESDFor electronics trays, nests and handling fixtures that must not build up static charge.48 MPa tensile
- ToughPick when snap-fits, clips, thin walls or drop-test parts need real ductility instead of brittle fracture.40 MPa yield · 78 Shore D
Working with ABS-Like-ESD
Is ABS-Like easy to machine?
Drills, taps and sands easily with sharp tools and low heat, but is notch-sensitive — pre-drill pilot holes, use light feeds and avoid clamping thin cured sections.
Can ABS-Like be welded?
Thermoset — cannot be heat welded; join with cyanoacrylate, epoxy or a drop of the same UV resin cured with a 405 nm lamp.
Can ABS-Like be formed, bent or molded?
Printed on 385/405 nm SLA/DLP/LCD at 25–35 °C vat temperature, then IPA-washed and UV/heat post-cured (typically 5–30 min at 40–60 °C) to reach datasheet strength; design 2 mm minimum walls and add drain holes for hollow parts.
What surface finishes work on ABS-Like?
Sands from 400 to 2000 grit and takes primer, spray paint, vacuum metallizing or electroplating well; always prime or clear-coat with UV blocker since bare parts yellow and embrittle in sunlight.
ABS-Like chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| aliphatic urethane acrylate oligomerbackbone toughness/elongation | 30 – 60 | 45 |
| epoxy acrylate / polyester acrylate oligstiffness and Tg | 0 – 25 | 10 |
| monofunctional acrylate monomer (IBOA, Hviscosity control | 15 – 40 | 28 |
| multifunctional acrylate crosslinker (HDcrosslink density | 5 – 20 | 12 |
| photoinitiator (TPO / TPO-L / BAPO)385/405 nm cure | 0.5 – 4 | 2 |
| pigment, dispersant, UV blocker, defoamecure-depth and appearance control | 0.3 – 3 | 1.5 |
| inorganic filler (silica / glass / talc)only in RIGID and FR variants | 0 – 40 | 0 |
ABS-Like-ESD — frequently asked
What is ABS-Like-ESD used for?
ABS-Like-ESD is typically used for consumer housings, drop-test prototypes, appearance and cosmetic models, assembly fit-check parts, covers and bezels and control-panel prototypes. In short: tough and impact-resistant; mirrors molded ABS.
What is the yield strength of ABS-Like-ESD?
ABS-Like-ESD has a typical yield strength of 45 MPa (6.53 ksi) and a tensile strength of 48 MPa (6.96 ksi) — weaker than 65% of polyurethane grades. Strength varies by condition: see the 7 listed tempers.
Is ABS-Like-ESD easy to machine?
Reasonably — machinability is rated good (55/100, worse than 67% of polyurethane grades). Drills, taps and sands easily with sharp tools and low heat, but is notch-sensitive — pre-drill pilot holes, use light feeds and avoid clamping thin cured sections.
Can ABS-Like-ESD be welded?
Not readily — weldability is rated not recommended (5/100). Thermoset — cannot be heat welded; join with cyanoacrylate, epoxy or a drop of the same UV resin cured with a 405 nm lamp.
What surface finishes work on ABS-Like-ESD?
Sands from 400 to 2000 grit and takes primer, spray paint, vacuum metallizing or electroplating well; always prime or clear-coat with UV blocker since bare parts yellow and embrittle in sunlight.
Can ABS-Like-ESD be formed, bent or molded?
Printed on 385/405 nm SLA/DLP/LCD at 25–35 °C vat temperature, then IPA-washed and UV/heat post-cured (typically 5–30 min at 40–60 °C) to reach datasheet strength; design 2 mm minimum walls and add drain holes for hollow parts.
What is the maximum service temperature of ABS-Like-ESD?
ABS-Like-ESD is rated for continuous use to about 55°C (131 °F), and briefly to 75°C. Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between ABS-Like-STD and ABS-Like Tough?
STD is the default condition — default choice for appearance models, fit-check parts and general functional prototypes at room temperature. Tough: pick when snap-fits, clips, thin walls or drop-test parts need real ductility instead of brittle fracture. Yield strength is 45 MPa in STD versus 40 MPa in Tough.
Can FabDigit make parts in ABS-Like-ESD?
Yes — ABS-Like-ESD is available for urethane casting with instant online pricing. Upload a STEP file to get a price and a DFM check.
Sources
- Formlabs Tough 2000 / Grey Pro photopolymer material data sheet — Formlabs (2023)
- Somos NeXt / Somos EvoLVe 128 stereolithography resin data — Covestro (DSM Somos) (2022)
- eSUN / Anycubic / Elegoo ABS-Like photopolymer resin TDS — eSUN, Anycubic, Elegoo (2024)
- ASTM D638 / D790 / D256 / D648 test methods for plastics — ASTM International (2022)
- Additive Manufacturing Technologies (vat photopolymerization chapter) — Springer (2021)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.