Clear Resin · grade
Clear Resin UV Resistant
Properties of the UV Resistant condition, compared with the other Clear Resin grades.
Use for parts with sunlight or lamp exposure where colour stability over months matters; slightly lower initial clarity and marginally softer cure.
What is Clear Resin UV Resistant?
Clear Resin UV Resistant is Clear Resin in the UV Resistant grade — use for parts with sunlight or lamp exposure where colour stability over months matters; slightly lower initial clarity and marginally softer cure. Clear Resin UV Resistant has a yield strength of 52 MPa (7.54 ksi) and a tensile strength of 62 MPa (8.99 ksi) — stronger than 52% of polymer grades. Elongation at break is 7.5% and the elastic modulus is 2.6 GPa (0.377 Msi). Clear Resin UV Resistant has a density of 1.19 g/cm³ (0.043 lb/in³), heavier than 52% of polymer grades. Its glass-transition temperature is 65°C (149 °F). Standard is the default condition FabDigit quotes; UV Resistant is available on request or by drawing note.
Advantages
- Polishes to a fine finish — 85/100, better than 93% of polymer grades
- Good UV / weathering resistance — 55/100, better than 77% of polymer grades
Limitations
- Limited formability — 5/100, worse than 95% of polymer grades
- Limited service temperature — 55°C (131 °F), worse than 91% of polymer grades
- Difficult to weld — 5/100, worse than 90% of polymer grades
- Low fracture toughness — 0.9 MPa·√m (0.819 ksi·√in), worse than 89% of polymer grades
- Needs corrosion protection — 65/100, worse than 88% of polymer grades
Clear Resin UV Resistant properties
Typical room-temperature values for Clear Resin UV Resistant — 11 properties are specific to this condition; the rest are grade-level values shared by every Clear Resin grade. Each bar shows where the value sits among the polymer grades in FabDigit's library — further right is higher.
Physical6
Clear Resin UV Resistant has a density of 1.19 g/cm³ (0.043 lb/in³), heavier than 52% of polymer grades. Its glass-transition temperature is 65°C (149 °F).
Mechanical14
Clear Resin UV Resistant has a yield strength of 52 MPa (7.54 ksi) and a tensile strength of 62 MPa (8.99 ksi) — stronger than 52% of polymer grades. Elongation at break is 7.5% and the elastic modulus is 2.6 GPa (0.377 Msi).
Thermal11
Clear Resin UV Resistant is rated for continuous service to 55°C (131 °F). It conducts heat at 0.2 W/m·K (0.116 BTU/hr·ft·°F), worse than 56% of polymer grades. Thermal expansion is 110 µm/m·K (61.1 µin/in·°F).
Electrical5
Clear Resin UV Resistant is an electrical insulator with a dielectric strength of 15 kV/mm (381 V/mil) and a resistivity of 1×10¹² Ω·m.
Chemical & Environmental3
Corrosion resistance is good (65/100), worse than 88% of polymer grades. UV resistance is good.
Sustainability3
Producing a kilogram of Clear Resin UV Resistant takes about 110 MJ of energy and emits 5.5 kg of CO₂ — more than 64% of polymer grades. Typical recycled content is 0%.
Manufacturability4
Clear Resin UV Resistant's machinability is fair (45/100, worse than 77% of polymer grades); weldability not recommended (5/100); formability not recommended (5/100).
Values are nominal handbook figures for design screening. Certified mill or lot data ships with every FabDigit order on request.
Other Clear Resin grades and fills
Clear Resin is also supplied in 4 other conditions. The full side-by-side table is on the Clear Resin overview.
- StandardDefaultDefault choice for transparent prototypes, fluid-flow models and see-through housings where clarity is cosmetic rather than optical.65 MPa tensile
- BiocompatibleChoose for dental splints, surgical guides and transparent devices needing ISO 10993 / USP Class VI documentation and validated post-cure.68 MPa tensile
- UV ResistantUse for parts with sunlight or lamp exposure where colour stability over months matters; slightly lower initial clarity and marginally softer cure.62 MPa tensile
- Optical GradePick when the part must transmit or guide light (lenses, light pipes, flow cells) and will be sanded/polished or vapour-clear-coated.60 MPa tensile
- As-PrintedOnly relevant for form/fit checks or parts to be bonded before cure — green strength and heat resistance are much lower and creep is significant.38 MPa tensile
Working with Clear Resin UV Resistant
Is Clear Resin easy to machine?
Drill and mill with sharp carbide, high speed, light feed and air cooling; the crosslinked resin is notch-sensitive and will craze or chip if heated or clamped hard.
Can Clear Resin be welded?
Thermoset — cannot be heat welded; join with UV-cure acrylate adhesive, cyanoacrylate or a drop of the same resin cured under a 405 nm lamp.
Can Clear Resin be formed, bent or molded?
Vat photopolymerization only: resin 25–35 °C, 25–100 µm layers, then IPA wash (keep soak short to avoid clouding/swelling) and 30–60 min 405 nm post-cure at 60–80 °C for full properties; expect ~0.2–0.5% cure shrinkage and warping in thick solid sections.
What surface finishes work on Clear Resin?
For clarity wet-sand 400→3000 grit then polish with plastic compound, or apply a thin clear UV/acrylic coat; avoid acetone and prolonged IPA, and add a UV-blocking topcoat if the part sees sunlight.
Clear Resin chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| urethane acrylate / epoxy acrylate oligobackbone oligomer, sets stiffness and toughness | 30 – 60 | 45 |
| photoinitiator (TPO / BAPO / Irgacure ty385/405 nm absorbing | 0.5 – 4 | 2 |
| UV absorber / light blockercontrols cure depth; higher in UV-resistant grade with HALS | 0 – 1 | 0.2 |
| additives (defoamer, stabilizer, chain-t | 0.1 – 3 | 1 |
| acrylate / methacrylate reactive monomere.g. HDDA, TPGDA, IBOA — controls viscosity and Tg | ≥ 30 (balance) | — |
Clear Resin UV Resistant — frequently asked
What is Clear Resin UV Resistant used for?
Clear Resin UV Resistant is typically used for optical prototypes, light pipes, LED diffusers and lens covers, fluidic and microfluidic test channels, sight glasses and inspection windows and transparent demonstration housings. In short: optically clear photopolymer.
What is the yield strength of Clear Resin UV Resistant?
Clear Resin UV Resistant has a typical yield strength of 52 MPa (7.54 ksi) and a tensile strength of 62 MPa (8.99 ksi) — stronger than 52% of polymer grades. Strength varies by condition: see the 5 listed tempers.
Is Clear Resin UV Resistant easy to machine?
Reasonably — machinability is rated fair (45/100, worse than 77% of polymer grades). Drill and mill with sharp carbide, high speed, light feed and air cooling; the crosslinked resin is notch-sensitive and will craze or chip if heated or clamped hard.
Can Clear Resin UV Resistant be welded?
Not readily — weldability is rated not recommended (5/100). Thermoset — cannot be heat welded; join with UV-cure acrylate adhesive, cyanoacrylate or a drop of the same resin cured under a 405 nm lamp.
What surface finishes work on Clear Resin UV Resistant?
For clarity wet-sand 400→3000 grit then polish with plastic compound, or apply a thin clear UV/acrylic coat; avoid acetone and prolonged IPA, and add a UV-blocking topcoat if the part sees sunlight.
Can Clear Resin UV Resistant be formed, bent or molded?
Vat photopolymerization only: resin 25–35 °C, 25–100 µm layers, then IPA wash (keep soak short to avoid clouding/swelling) and 30–60 min 405 nm post-cure at 60–80 °C for full properties; expect ~0.2–0.5% cure shrinkage and warping in thick solid sections.
What is the maximum service temperature of Clear Resin UV Resistant?
Clear Resin UV Resistant is rated for continuous use to about 55°C (131 °F), and briefly to 85°C. Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Can FabDigit make parts in Clear Resin UV Resistant?
Yes — Clear Resin UV Resistant is available for injection molding and 3D printing with instant online pricing. Upload a STEP file to get a price and a DFM check.
Sources
- Clear Resin photopolymer technical data sheet (SLA/LFS) — Formlabs (2023)
- ASTM D638 / D790 / D256 / D648 test methods for plastics — ASTM International (2022)
- Photopolymers: Chemistry and Properties of UV-curable acrylate systems — Wiley / SpecialChem technical literature (2019)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.