Machining-Friendly Cu Alloy · Leaded Brass
Copper Alloy C35300
Copper Alloy C35300 is a machining-friendly copper alloy — standard screw-machine brass. Typical values: 125 MPa yield, 8.55 g/cm³, rated to 200 °C. Available for CNC machining at FabDigit.
Properties
Typical room-temperature values in the H02 (half Hard) condition. Metric first, imperial in gray. The bars show where C35300 sits against the other 36 copper alloy grades in the catalog.
Datasheet
| Yield strength | 125 MPa18 ksi |
|---|---|
| Tensile strength | 360 MPa52 ksi |
| Hardness | 65 HRB≈ 114 HB |
| Density | 8.55 g/cm³0.309 lb/in³ |
| Specific strength (yield ÷ density) | 15 |
| Min service temp | -200 °C-328 °F |
| Max service temp | 200 °C392 °F |
| Electrical conductivity | 26 % IACS15.1 MS/m |
| Machinability | Excellent90 / 100 |
| Weldability | Not recommended5 / 100 |
| Formability | Fair50 / 100 |
| ISO 513 machining group | N |
Values are nominal handbook figures for design screening. Certified mill or lot data ships with every FabDigit order on request.
Against other copper alloy grades
Strength versus weight in the copper alloy family
Yield strength against density for every copper alloy grade FabDigit runs. C35300 is highlighted; hover a dot for its name, or open the interactive family chart.
Manufacturability
The process limits FabDigit's quote engine applies to C35300. Design inside these and the part quotes instantly; outside them it routes to an engineer.
CNC machining
| Machinability | Excellent90 / 100 |
|---|---|
| ISO material group | N.5 |
| Cutting speed (rough / finish) | 180 / 220 m/min |
| Minimum wall | 0.8 mm |
| Minimum internal radius | 1 mm |
| Drill depth limit | 6× diameter |
| Best surface (machined / polished) | Ra 1.6 / — |
| Hardenable after machining | No |
Conditions and tempers
How C35300 is supplied and what each state is for. The default is what FabDigit quotes unless your drawing says otherwise.
| Condition | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness |
|---|---|---|---|---|---|
H02Default Half Hard (H02) | Half-hard brass/copper — fittings and terminals with slight spring | — | — | — | — |
Heat treatment and post-processing
Operations FabDigit's suppliers routinely run on C35300, ranked by how often they make sense for this grade.
Heat treatment
| Full Anneal | Restore ductility; relieve residual stress; coarsen grain |
|---|---|
| Stress Relief | Reduce residual stress without changing structure |
| Age C17200 (Beryllium Cu) | Cu-Be peak strength (TF00) |
Post-processing
| Manual Deburr | Deburrstandard |
|---|---|
| Edge Break (0.5mm) | Deburr |
| CMM Inspection | Inspection |
| FAI Report | Inspection |
| Individual Bag | Packaging |
Surface finishes for C35300
Coatings and treatments compatible with copper alloy on the processes C35300 runs on. Pick them in the quote configurator or call them out on the drawing.
Passivation
- Electropolishing
Plating
- Chrome Plating
- Copper Plating
- Electroless Nickel (EN)
- Gold Plating
- Nickel Plating
- Silver Plating
- Tin Plating
Organic Coating
- Painting
Marking / Decoration
- Chemical Etching
- Dot Peen Marking
- Electro-chemical Etching
- Ink Stamping
- Laser Marking
- Mechanical Engraving
- Steel Stamping
- Vibro Engraving / Scribing
Equivalent designations
Standards and trade names that resolve to Copper Alloy C35300 in FabDigit's catalog. Equivalence is nominal — check the exact specification when certification matters.
- Also called
- High-Leaded Brass
- Other
- 353
Stock forms
Raw-material forms FabDigit sources C35300 in.
Property data is compiled from published supplier and standards handbooks and normalised for comparison; hardness values on non-Brinell scales are converted approximately for charting only. Manufacturability limits are FabDigit quote-engine defaults and may be relaxed by engineering review. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.