Twaron · grade

Twaron 2200-HM

Properties of the 2200-HM condition, compared with the other Twaron grades.

Choose where stiffness and low creep matter: optical-cable strength members, composite reinforcement, tension members.

High cost $$$$

Request a quote in Twaron 2200-HM Twaron overview

What is Twaron 2200-HM?

Twaron 2200-HM is Twaron in the 2200-HM grade — choose where stiffness and low creep matter: optical-cable strength members, composite reinforcement, tension members. Twaron 2200-HM has a tensile strength of 3,200 MPa (464 ksi), stronger than 83% of composite grades. Elongation at break is 2.6% and the elastic modulus is 115 GPa (16.7 Msi). Twaron 2200-HM has a density of 1.45 g/cm³ (0.0524 lb/in³), lighter than 61% of composite grades. Its glass-transition temperature is 340°C (644 °F). 1000 is the default condition FabDigit quotes; 2200-HM is available on request or by drawing note.

Limitations

Degrades in UV without stabilisers — 20/100, worse than 94% of composite grades
Absorbs moisture — dry before molding — 3.5%, worse than 93% of composite grades
Poor heat conductor — 0.05 W/m·K (0.0289 BTU/hr·ft·°F), worse than 87% of composite grades

Twaron 2200-HM properties

Typical room-temperature values for Twaron 2200-HM — 6 properties are specific to this condition; the rest are grade-level values shared by every Twaron grade. Each bar shows where the value sits among the composite grades in FabDigit's library — further right is higher.

Physical3

Twaron 2200-HM has a density of 1.45 g/cm³ (0.0524 lb/in³), lighter than 61% of composite grades. Its glass-transition temperature is 340°C (644 °F).

Density1.45 g/cm³0.05 lb/in³

Glass Transition (Tg)340°C644 °F

Water Absorption (24 h)3.5%

Mechanical6

Twaron 2200-HM has a tensile strength of 3,200 MPa (464 ksi), stronger than 83% of composite grades. Elongation at break is 2.6% and the elastic modulus is 115 GPa (16.7 Msi).

Elastic (Young's) Modulus115 GPa16.7 Msi

Shear Modulus2.9 GPa0.42 Msi

Poisson's Ratio0.36

Tensile Strength (Ultimate)3,200 MPa464 ksi

Elongation at Break2.6%

Compressive Strength400 MPa58 ksi

Thermal8

Twaron 2200-HM is rated for continuous service to 180°C (356 °F). It conducts heat at 0.05 W/m·K (0.0289 BTU/hr·ft·°F), worse than 87% of composite grades. Thermal expansion is -4.5 µm/m·K (-2.5 µin/in·°F).

Thermal Conductivity0.05 W/m·K0.03 BTU/hr·ft·°F

Specific Heat Capacity1,420 J/kg·K0.34 BTU/lb·°F

Thermal Expansion (CTE, 20–100 °C)-4.5 µm/m·K-2.5 µin/in·°F

Max Service Temperature (continuous)180°C356 °F

Min Service Temperature-196°C-321 °F

Flammability (UL 94)Self-extinguishing, non-melting and non-dripping; carbonizes rather than melts, LOI ≈ 29 %

Limiting Oxygen Index29%

Max Service Temperature (short-term)250°C482 °F

Electrical3

Twaron 2200-HM has an electrical resistivity of 1×10¹² Ω·m.

Electrical Resistivity1×10¹² Ω·m3.94×10¹⁹ µΩ·in

Dielectric Constant (1 MHz)4

Volume Resistivity1×10¹⁴ Ω·cm

Chemical & Environmental3

Corrosion resistance is very good (80/100), better than 54% of composite grades. UV resistance is poor.

Corrosion ResistanceVery good80/100

UV / Weathering ResistancePoor20/100

Chemical Resistance SummaryExcellent against hydrocarbons, oils, most organic solvents and neutral salts; attacked by strong mineral acids, concentrated alkalis, hypochlorite bleach and hot steam (hydrolysis); must be shielded from sunlight/UV.

Sustainability4

Producing a kilogram of Twaron 2200-HM takes about 280 MJ of energy and emits 16 kg of CO₂ — more than 62% of composite grades. Typical recycled content is 0%.

Embodied Energy (primary production)280 MJ/kg120,378 BTU/lb

Embodied Carbon (primary production)16 kg CO₂/kg

Embodied Water400 L/kg47.9 gal/lb

Typical Recycled Content0%

Manufacturability1

Twaron 2200-HM's machinability is poor (25/100, worse than 65% of composite grades).

MachinabilityPoor25/100

Values are nominal handbook figures for design screening. Certified mill or lot data ships with every FabDigit order on request.

Other Twaron grades and fills

Twaron is also supplied in 9 other conditions. The full side-by-side table is on the Twaron overview.

1000DefaultGeneral-purpose para-aramid yarn for ropes, cables, protective textiles and rubber reinforcement.3,100 MPa tensile
AFRP-UDStructural AFRP for impact-tolerant, lightweight panels where low compressive strength is acceptable.1,350 MPa tensile
2200-HMChoose where stiffness and low creep matter: optical-cable strength members, composite reinforcement, tension members.3,200 MPa tensile

Working with Twaron 2200-HM

Is Twaron easy to machine?

Cuts fuzz badly — use serrated/hot knives, sharp carbide or PCD tools with high rake and backing plate, or abrasive waterjet; expect rapid tool dulling and hairy edges.

Can Twaron be welded?

Not weldable; joints are made by knotting/splicing, RFL adhesive bonding to rubber, or resin bonding in laminates.

Can Twaron be formed, bent or molded?

Processed by weaving, braiding, filament winding, pultrusion and prepreg lay-up; dry fibre must be conditioned (moisture ≤ 1 %) and vacuum-dried before resin infusion to avoid voids.

What surface finishes work on Twaron?

Difficult to dye (usually solution- or pigment-coloured); requires UV-blocking jacket, coating or paint for outdoor service; surface plasma/epoxy sizing improves resin adhesion.

Twaron chemical composition (wt %)

Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.

Element	Spec limit (wt %)	Nominal
p-phenylenediamine (PPD) repeat unitone of the two PPTA backbone monomers	≈ 50	50
terephthaloyl (TDC/terephthalic) repeat one of the two PPTA backbone monomers	≈ 50	50
spin finish / surface treatmentspin finish or adhesive-activation treatment, varies by product	0.2 – 1.5	0.6

Twaron 2200-HM — frequently asked

What is Twaron 2200-HM used for?

Twaron 2200-HM is typically used for ballistic protection, ropes and cables, friction/gasket materials and composite reinforcement. In short: direct Kevlar equivalent; broadest aramid form range; widely stocked in Europe.

What is the tensile strength of Twaron 2200-HM?

Twaron 2200-HM has a typical tensile strength of 3,200 MPa (464 ksi) — stronger than 83% of composite grades. Strength varies by condition: see the 10 listed tempers.

Is Twaron 2200-HM easy to machine?

Not especially — machinability is rated poor (25/100, worse than 65% of composite grades). Cuts fuzz badly — use serrated/hot knives, sharp carbide or PCD tools with high rake and backing plate, or abrasive waterjet; expect rapid tool dulling and hairy edges.

Can Twaron 2200-HM be welded?

Not weldable; joints are made by knotting/splicing, RFL adhesive bonding to rubber, or resin bonding in laminates.

What surface finishes work on Twaron 2200-HM?

Difficult to dye (usually solution- or pigment-coloured); requires UV-blocking jacket, coating or paint for outdoor service; surface plasma/epoxy sizing improves resin adhesion.

Can Twaron 2200-HM be formed, bent or molded?

Processed by weaving, braiding, filament winding, pultrusion and prepreg lay-up; dry fibre must be conditioned (moisture ≤ 1 %) and vacuum-dried before resin infusion to avoid voids.

What is the maximum service temperature of Twaron 2200-HM?

Twaron 2200-HM is rated for continuous use to about 180°C (356 °F), and briefly to 250°C. Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.

Sources

Twaron Product Brochure & Technical Guide (yarn, staple, short-cut, pulp) — Teijin Aramid (2022)
ASM Engineered Materials Handbook Vol. 1: Composites — ASM International (1987)
MMPDS / composite lamina typical property tables (aramid/epoxy) — Battelle (2021)

Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.