Corrosion Resistant AL · 5xxx
Aluminum 5652
Aluminum 5652 is a corrosion resistant aluminum — hydrogen peroxide-grade 5052. Typical values: 90 MPa yield, 2.67 g/cm³, rated to 65 °C. Available for CNC machining, Sheet metal at FabDigit.
Properties
Typical room-temperature values for the default supply condition. Metric first, imperial in gray. The bars show where 5652 sits against the other 163 aluminum grades in the catalog.
Datasheet
| Yield strength | 90 MPa13 ksi |
|---|---|
| Tensile strength | 195 MPa28 ksi |
| Hardness | 47 HB |
| Density | 2.67 g/cm³0.096 lb/in³ |
| Specific strength (yield ÷ density) | 34 |
| Min service temp | -200 °C-328 °F |
| Max service temp | 65 °C149 °F |
| Electrical conductivity | 31 % IACS18 MS/m |
| Machinability | Good60 / 100 |
| Weldability | Excellent85 / 100 |
| Formability | Excellent90 / 100 |
| ISO 513 machining group | N |
Values are nominal handbook figures for design screening. Certified mill or lot data ships with every FabDigit order on request.
Against other aluminum grades
Strength versus weight in the aluminum family
Yield strength against density for every aluminum grade FabDigit runs. 5652 is highlighted; hover a dot for its name, or open the interactive family chart.
Manufacturability
The process limits FabDigit's quote engine applies to 5652. Design inside these and the part quotes instantly; outside them it routes to an engineer.
CNC machining
| Machinability | Better60 / 100 |
|---|---|
| ISO material group | N.1 |
| Cutting speed (rough / finish) | 350 / 420 m/min |
| Minimum wall | 0.5 mm |
| Minimum internal radius | 1 mm |
| Drill depth limit | 8× diameter |
| Best surface (machined / polished) | Ra 0.8 / — |
| Hardenable after machining | No |
Sheet metal
| Formability | Excellent90 / 100 |
|---|---|
| Weldability | Better85 / 100 |
| Bendable | Yes |
Conditions and tempers
How 5652 is supplied and what each state is for. The default is what FabDigit quotes unless your drawing says otherwise.
| Condition | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness |
|---|---|---|---|---|---|
O Annealed (O) | Softest — parts you will bend or deep-form; not for carrying load | — | — | — | — |
H32 Strain hardened, partially annealed (H32) | Marine sheet with moderate forming — boat panels, tanks | — | — | — | — |
Heat treatment and post-processing
Operations FabDigit's suppliers routinely run on 5652, ranked by how often they make sense for this grade.
Heat treatment
| Age T6 (Aluminum) | Solution + artificial age to peak strength |
|---|---|
| Age T651 (Aluminum) | T6 + stress relief stretch (plate) |
| Full Anneal | Restore ductility; relieve residual stress; coarsen grain |
| Stress Relief | Reduce residual stress without changing structure |
| Age T73 (Aluminum) | Over-age 7000 for SCC resistance |
Post-processing
| Manual Deburr | Deburrstandard |
|---|---|
| Edge Break (0.5mm) | Deburr |
| Glass Bead Blast | Blast |
| Laser Mark | Marking |
| Sand Blast | Blast |
| Vibratory Tumble | Tumble |
| CMM Inspection | Inspection |
| Masking | Masking |
| Tap After Finish | Finish Fix |
| FAI Report | Inspection |
Surface finishes for 5652
Coatings and treatments compatible with aluminum on the processes 5652 runs on. Pick them in the quote configurator or call them out on the drawing.
Passivation
- Electropolishing
Conversion Coating
- Anodizing Type II
- Chem Film (Alodine)
- Hard Anodize Type III w/ PTFE
- Hard Anodizing Type III
Plating
- Electroless Nickel (EN)
- Gold Plating
- Nickel Plating
- Silver Plating
Organic Coating
- Cerakote
- E-Coating
- Epoxy Coating
- Painting
- Powder Coating
- PTFE Coating
PVD Coating
- DLC
Marking / Decoration
- Chemical Etching
- Dot Peen Marking
- Electro-chemical Etching
- Embossing / Debossing
- Ink Stamping
- Laser Marking
- Mechanical Engraving
- Steel Stamping
- Vibro Engraving / Scribing
Equivalent designations
Standards and trade names that resolve to Aluminum 5652 in FabDigit's catalog. Equivalence is nominal — check the exact specification when certification matters.
- Aluminum Association
- AA5652
- EN / DIN / Werkstoff-Nr.
- AW-5652AW 5652
- Other
- AW5652
Stock forms
Raw-material forms FabDigit sources 5652 in.
Property data is compiled from published supplier and standards handbooks and normalised for comparison; hardness values on non-Brinell scales are converted approximately for charting only. Manufacturability limits are FabDigit quote-engine defaults and may be relaxed by engineering review. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.